การพัฒนาวัสดุผสมซีเมนต์เสริมเส้นใยโดยใช้เส้นใยธรรมชาติจากขนสัตว์

Development of Fiber Reinforced Cement Composites Using Natural Fibers from Animal Hair

Name: ทวี มูลแก้ว

Organization : มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. คณะวิศวกรรมศาสตร์. สาขาวิชาวิศวกรรมโยธา

keyword: คอนกรีตเสริมไฟเบอร์

; Reinforced concrete, Fiber

; การแตกร้าว

Abstract: The objective of this thesis is to study the control of plastic shrinkage cracking of concrete using animalhairfibers compared with that of using polypropylene fibers, and to study the possibility in using animalhairfibers to enhance the tensile strength of mortar. This research consists of three main parts. Part I is tofind the properties of the animal-hair fibers. Part II focuses on the study to control plastic shrinkagecracking of concrete being in severe environmental conditions by using the fibers. The experiments weredone in well-arranged room with controlling temperature and relative humidity. Fiber volume fractionused is between 0.05-0.25 percent. Part I11 deals with the investigation of mechanical properties of fiberreinforced cement composites. This part includes: (a) compressive strength of concrete adding fibersbetween 0.05-0.25 percent; (b) compressive strength of mortar adding fibers between 0.10-2.0 percent;and (c) flexural behavior of mortar when fibers were added at 2.0 percent. The test results showed thatthe use of animal-hair fibers at volume hction of 0.25 percent was able to reduce plastic shrinkagecracking more than 80 percent compared with plain concrete and this was equivalent to the use ofpolypropylene fibers; however, the compressive strength of concrete decreased approximately 5.0percent. When a large volume of fibers were used at between 0.10-2.0 percent, the compressive strengthof mortar decreased between 28-49 percent. The results of flexural tests showed that fibers had noinfluence on the cracking strength, whereas the strain enera up to failure increased 11 percent with theuse of animal-hair fibers and inmased more than 110 percent with the use of polypropylene fibers.

มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. สำนักหอสมุด

Address: กรุงเทพมหานคร (Bangkok)

Email: info.lib@mail.kmutt.ac.th

Name: ชูชัย สุจิวรกุล

Role: อาจารย์ที่ปรึกษา

Created: 2547

Issued: 2007-06-21

Modified: 2007-07-19

วิทยานิพนธ์/Thesis

ISBN: 9741839251

CallNumber: CVE2183

tha

DegreeName: วิศวกรรมศาสตรมหาบัณฑิต

Level: ปริญญาโท

Descipline: วิศวกรรมโยธา

Grantor: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

©copyrights มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	CVE2183.pdf	4.76 MB	168	2025-01-21 23:15:08
2	CVE2183ab.pdf	28.01 KB	51	2020-11-01 12:44:06
3	CVE2183ab.txt	2.04 KB	34	2018-07-06 13:13:10

ใช้เวลา

0.049949 วินาที