Effect of SEBS Copolymers on The Interfacial Strength Between Polystyrene and Low Density Polyethylene

Name: Chatchai Kunyawut

Address: Pathumthani

Organization : Rajamangala Institute of Techonology. Faculty of Engineering

Name: Julia S. Higgins

Address: Pathumthani

Organization : Rajamangala Institute of Techonology. Faculty of Engineering

ThaSH: AFM

ThaSH: SEBS

ThaSH: Polymers

Abstract: The relative interfacial strengths of poly (styreneblock-ethylene!butylene-block-styrene) triblock copolymers (SEBS) modified interfaces of immiscible polymers. polystyrene (PS) and low density polystyrene (LOPE). has been studied using peel test. Specimens were prepared by spin coating thin SEBS triblock copolymer films from solution onto LOPE slab. After spin coating and drying in a vacuum oven at 40 degree Celsius for several days. the LOPE slabs were placed on top of them. forming the "sandwich" arrangement. The 90 degree Celsius peel test arrangement was employed because the PS is stiff at room temperature whereas the LOPE is flexible. For thin copolymer layer (expected to leave the interface unsaturated). the trend in variation of interfacial strength with copolymer molecular weight was observed. However. for thick layers (oversaturating interface) the interfacial strength became in one case too large to separate the layers in the peel test. This may suggest a different mechanism for increasing interfacial strength when at least one of the copolymer blocks is crystallisable. Moreover. The microstructure morphology of the copolymers at the interface is expected to change during annealing time since it was found that the interfacial strength changed with annealing time.

Rajamangala University of Technology Thanyaburi

Address: PATHUM THANI

Email: elibrary@mail.rmutt.ac.th

Modified: 2015-02-11

Issued: 2558-02-11

บทความ/Article

application/pdf

ISBN: 1685-5280

BibliograpyCitation : Journal of Engineering. RMUTT Volume 4, Issue 7 (Jan - Jun 2006), p.101-112

eng

©copyrights Rajamangala Univetsity of Technology Thanyaburi

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	Journal of Engineering Y.04 Vol.7 p.101-112 2006.pdf	5.51 MB	4	2018-06-04 02:44:34

ใช้เวลา

0.019731 วินาที